Research description of boron-free ramming mass materials for induction furnace  The main failure forms of furnace lining mainly include the following: 1. Thermal stress cracking, furnace lining in the use process of use, the lining contacts high temperature metal liquid, the outer layer is close to the water cooling coil, the temperature difference is huge, after the periodic cold and heat cycle, cause volume expansion and contraction, easy to lead to the furnace lining thermal stress cracking, expansion and peeling phenomenon. 2. Chemical erosion, C and FeO in steel water form a chemical reaction with the furnace lining at high temperature, SIO2 + 2C —> SI + 2CO, SIO2 is reduced by C; FEO and SIO2 to FEO.SIO2 low melt at about 1170 degrees, quickly separated from the furnace lining under the stirring of high temperature steel water. 3, Electromagnetic mixing and local overheating caused by mechanical erosion, furnace lining is in the process of steel water contact, local may appear a series of chemical and physical reaction, cause local overheating, form local liquid phase, in electromagnetic stirring, and steel water erosion process, easy to form furnace lining defect, cracking, in cracking and defect is prone to appear furnace lining...

Yiwu shoumai e-commerce company design the refractory layer of DC EAF type of Enrichment of platinum project is running successful . this project is chinese first DC EAF Enrichment of platinum project . this DC EAF working temp : 2000 'C , melt liquid temp : 1750'C

对于高温下活泼金属熔融炉耐材衬，对传统耐火材料提出了新的要求，活泼金属或双氧型金属熔融液体以及强腐蚀型金属液体，传统的镁，铝，碳质耐火材料都不能在高温下满足他们的熔炼需求，在工业化要求长时间连续作业的要求下，无法满足满足长时间连续生产的负荷。

我公司结合欧美市场针对隧道窑的设计需求，以降低现场劳动成本为出发点。生产完成隧道用整体预制大块，最大预制尺寸：4.5米*2.4米 。同时开发了吊装结构，解决现场施工问题。

铁水罐砖衬与渣铁水（主要是铁水）直接接触，温度较高，铁水罐砖衬受侵蚀、损坏主要表现：l)铁水罐底部砖衬受高落差下降铁水冲蚀作用。2)圆周砖衬受高温渣铁的化学侵蚀反应 。3)装铁水时温度急剧升高热震作用。

我司采用铬锆复合材质针对镍铁固定高温炉所需组合式匣钵进行研发，完成首套组合式匣钵生产。铬锆复合材质针对镍铁固定高温炉使用温度>1650度，进行研发。满足镍铁固定炉生产工况，解决了物料冲刷以及高温下耐材在氧化气氛中的自身反应等问题。

Cr2O3化学性质稳定，耐酸碱、高温性质稳定，具有很高的硬度和良好的耐火性能。在高温下，Cr3+会被部分地转变为Cr2+，从而使Cr2O3的熔点降低。因此，Cr2O3的熔点还没有统一的意见，只有一个温度范围2265~2330℃。尽管如此，具有如此高的熔点范围，在耐火材料中的应用是足够的。

结合最新耐火材料高流性浇筑成型技术-解决匹萨炉预制表面气孔问题，成本预制件表面气孔率达到1%。以下，搭配梯度降温技术 – 解决原设计保温层厚度以及施工不便问题，采用纳米隔热反射技术，减少热量散发，窑内温度500度，窑皮温度30度以下，根据欧盟食品安全标准，经过8个月研发，全预制高效节能保温匹萨炉定型，这也是我司继老干妈贵定厂区炉灶项目后，第二个食品级工业耐火材料项目。